| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.20 | g/cm3 | |
| 熔流率（熔体流动速率） | 300°C/1.2 kg | ASTM D1238 | 8.0 | g/10 min | |
| 收缩率 - 流动 | ASTM D955 | 0.50 到 0.70 | % | ||
| 吸水率 | 23°C, 24 hr | ASTM D570 | 0.15 | % | |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 | % | ||
| 机械性能 | 洛氏硬度 | M 级 | ASTM D785 | 73 | |
| R 级 | ASTM D785 | 118 | |||
| 拉伸模量 | ASTM D638 | 2410 | MPa | ||
| 抗张强度 | 屈服, 23°C 3 | ASTM D638 | 60.0 | MPa | |
| 断裂 | ASTM D638 | 72.0 | MPa | ||
| 伸长率 | 屈服 | ASTM D638 | 6.0 | % | |
| 断裂 | ASTM D638 | 150 | % | ||
| 弯曲模量 | ASTM D790 | 2410 | MPa | ||
| 弯曲强度 | ASTM D790 | 96.0 | MPa | ||
| 耐磨耗性 - Change in Haze 4 | ASTM D1001 | 45 | % | ||
| 悬壁梁缺口冲击强度 5 | 23°C, 3.20 mm | ASTM D256 | 900 | J/m | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D256 | 无断裂 | ||
| 装有测量仪表的落镖冲击 6 | 23°C, 3.20 mm, Total Energy | ASTM D3763 | 89.0 | J | |
| 热性能 | 载荷下热变形温度 | 0.45 MPa, 退火, 4.00 mm | ASTM D648 | 144 | ℃ |
| 1.8 MPa, 未退火, 4.00 mm | ASTM D648 | 128 | ℃ | ||
| 1.8 MPa, 退火, 4.00 mm | ASTM D648 | 141 | ℃ | ||
| 维卡软化温度 | ASTM D1525 7 | 150 | ℃ | ||
| 球压温度 | IEC 60598-1 | > 125 | ℃ | ||
| 线形热膨胀系数 - 流动 | -40 到 82°C | ASTM D696 | 6.8E-5 | cm/cm/℃ | |
| 电气性能 | 体积电阻率 | 23°C | ASTM D257 | 2.0E+17 | ohm·cm |
| 介电强度 | ASTM D149 | 17 | kV/mm | ||
| 介电常数 | 60 Hz | ASTM D150 | 3.00 | ||
| 介电常数 | 60 Hz | ASTM D150 | 1.0E-3 | ||
| 耗散因数 | IEC 60112 | 250 | V | ||
| 漏电起痕指数 | 2.00 mm | ||||
| 其它性能 | UL 阻燃等级 | 3.00 mm | UL 94 | HB | |
| 0.500 mm | UL 94 | V-2 | |||
| 1.60 mm | UL 94 | V-2 | |||
| 2.50 mm | UL 94 | V-2 | |||
| 3.00 mm | UL 94 | V-2 | |||
| 热灯丝点火温度 8 | 2.00 mm | IEC 60695-2-13 | 850 | °C | |
| 极限氧指数 | ASTM D2863 | 26 | % | ||
| 平均燃烧程度 | ASTM D635 | 3 | cm | ||
| 光学性能 | 折射率 | ASTM D542 | 1.586 | ||
| 透射率 | ASTM D1003 | 89.0 | % | ||
| 雾度 | ASTM D1003 | 0.70 到 1.5 | % | ||